如果彩涂铝板加工后的颜色的实际效果不能超过估计的实际效果，将对其应用造成相当大的危害。在制造中，影响彩涂铝板加工表面的色差有哪些?铝板加工厂家为您讲解。
If the actual effect of the color of the color coated aluminum plate after processing cannot exceed the estimated actual effect, it will cause considerable harm to its application. In manufacturing, what are the color differences that affect the processing surface of color-coated aluminum plate? The aluminum plate processing factory will explain to you.
1.染色水溶液温度。
1. Dyeing water solution temperature.
铝板的染色分为冷染色和热染色。冷染在加工过程中使用时间较长，所以对色彩对称性的把握很好。热染色的使用时间较短，但没有办法控制颜色。热染色温度一般为40℃和60℃。如果温度过高，则会降低染色的吸收率，很容易使铝板表面充分绽放。
The dyeing of aluminum plate is divided into cold dyeing and hot dyeing. Cold dyeing is used for a long time in the processing process, so the color symmetry is well grasped. The use time of thermal dyeing is short, but there is no way to control the color. The thermal dyeing temperature is generally 40 ℃ and 60 ℃. If the temperature is too high, the absorption rate of dyeing will be reduced, and it is easy to make the surface of aluminum plate fully bloom.
2.空气氧化膜对铝单板质量的危害。
2. The harm of air oxide film to the quality of aluminum veneer.
空气氧化膜是指铝单板的厚度、孔隙率和透明度。铝板内空气氧化膜的厚度可维持在10μm左右，从而获得孔隙率和透明度，获得较好的染色质量。
Air oxide film refers to the thickness, porosity and transparency of aluminum veneer. The thickness of air oxide film in aluminum plate can be maintained at 10 μ M to obtain porosity and transparency and better dyeing quality.

3.染色溶液浓度。
3. Dyeing solution concentration.
染色剂的浓度与染色剂有关。铝单板上色后，浓度较低，轻浓度稍高。如果浓度过高，会造成颜色不均匀或上下波动，这在清洗和关闭“流体颜色”的整个过程中很容易发生。为了提高染料对染料的吸收能力，选择低浓度的颜色增加染色，使染料分子结构更均匀地进入空气氧化膜孔中，使颜色更协调强。
The concentration of dye is related to the dye. After the aluminum veneer is colored, the concentration is lower, and the light concentration is slightly higher. If the concentration is too high, it will cause uneven color or fluctuation, which is easy to occur during the whole process of cleaning and closing the "fluid color". In order to improve the absorption capacity of the dye to the dye, select the color with low concentration to increase the dyeing, so that the molecular structure of the dye can enter the air oxide film hole more evenly, and make the color more harmonious and strong.
4.铝型材双板零件原材料的危害。
4. Hazards of raw materials of aluminum profile double-plate parts.
正常情况下，高纯铝、铝镁、铝锰铝合金在氧化处理过程中，其染色特性好，可染成多种颜色。对于硅或铜重板，在整个染色过程中只有深褐色和灰黑色，颜色比较简单。
Under normal conditions, high-purity aluminum, aluminum-magnesium, aluminum-manganese aluminum alloys have good dyeing characteristics and can be dyed into various colors during oxidation treatment. For silicon or copper heavy plates, there are only dark brown and gray black in the whole dyeing process, and the color is relatively simple.
哪些原因会影响到彩涂铝板加工的色差？我们从四个方面来讲解了这个问题，您有何疑惑或者需求可以随时来我们网站http://www.jndclyyxgs.com咨询！
What causes will affect the color difference of color coated aluminum plate processing? We have explained this problem from four aspects. If you have any doubts or needs, please come to our website at any time http://www.jndclyyxgs.com consulting service