合金铝板的压型加工工艺介绍

来源:http://www.jndclyyxgs.com/ 发布时间:2024-02-05

合金铝板压型加工时是铝卷在压型设备(彩钢瓦设备)上面加工,类似于滚边、折边加工工艺,将铝板加工为各种型号的压型铝板,主要用于屋面、电厂脱硫、防腐保温等行业中。

During the compression processing of alloy aluminum sheets, aluminum coils are processed on the compression equipment (color steel tile equipment), similar to the rolling and folding processing technology. The aluminum sheets are processed into various types of compression aluminum sheets, mainly used in industries such as roofs, power plant desulfurization, anti-corrosion and insulation.

铝板压型加工的常见规格:通常铝板都是压型YX35-125-750型号为常用,尤其是电厂防腐保温工程、烟道脱硫防腐工程为常用,厚度以0.5-1.2mm厚度居多,材质常常为1060、3003、3A21、LF21等材质。

Common specifications for aluminum plate pressing processing: Usually, YX35-125-750 aluminum plates are commonly used, especially in power plant anti-corrosion and insulation engineering, flue desulfurization and anti-corrosion engineering. The thickness is mostly 0.5-1.2mm, and the materials are often 1060, 3003, 3A21, LF21, and other materials.

第二种常见的铝板压型加工型号为YX23-210-840型号,常常拥有屋面和墙面方面,我们称为840型压型铝板,有时候许多工厂和车间的屋面采用彩涂铝卷进行压型常常选择840型号的压型铝板。

20230531034346643.jpg

The second common aluminum plate pressing processing model is YX23-210-840 model, which often has roof and wall aspects. We call it 840 type pressed aluminum plate. Sometimes, many factories and workshops use colored coated aluminum coils for pressing on the roof, and often choose 840 type pressed aluminum plate.

铝板在压型加工过程中要注意压型铝板的长度和厚度,避免因为设备问题导致的压型铝板边缘部位因为磨损导致的毛刺。在铝板的压型加工以后包装的适合也要注意防水防潮。同时在选择铝板材质方面建议不要选择硬度太高的产品,通常可选择H24或者H16状态的铝卷作为铝板压型加工的原料,如果铝板硬度太高会导致加工过程中断裂问题。

During the pressing process of aluminum plates, attention should be paid to the length and thickness of the pressed aluminum plates to avoid burrs at the edges of the pressed aluminum plates caused by wear and tear due to equipment issues. After the compression processing of the aluminum plate, the packaging should also pay attention to waterproofing and moisture prevention. At the same time, it is recommended not to choose products with high hardness when selecting aluminum plate materials. Generally, aluminum coils in H24 or H16 state can be selected as the raw material for aluminum plate pressing processing. If the aluminum plate hardness is too high, it will cause fracture problems during the processing.

压型加工中常见问题:压型加工中的问题主要是铝卷平整度不行,容易跑偏,所以想要压型过程中不跑偏建议采用拉弯矫处理,校平平整度,就能够很好的避免铝板压型过程中的跑偏。山东泰格铝业有限公司常年提供各种优质的压型铝板,适合于电力、屋面、设备罐体等各种设备使用,现货供应厚度0.5毫米、0.6毫米、0.7毫米、0.8毫米、1毫米等各种厚度的压型铝板和

Common problems in compression molding: The main problem in compression molding is the poor flatness of the aluminum coil, which is prone to deviation. Therefore, if you want to avoid deviation during the compression process, it is recommended to use tension bending correction to level the flatness, which can effectively avoid deviation during the aluminum plate compression process. Shandong Taige Aluminum Industry Co., Ltd. provides various high-quality profiled aluminum sheets year-round, suitable for use in various equipment such as power, roofs, and equipment tanks. In stock, we supply profiled aluminum sheets with thicknesses of 0.5mm, 0.6mm, 0.7mm, 0.8mm, 1mm, and other thicknesses